7075-T651 aircraft aluminum plate refers to the state of 7075 aluminum alloy after solution treatment and then artificial aging treatment.
In this state, 7075 aluminum alloy has good strength and corrosion resistance, and is suitable for aerospace and high-end machinery fields.
7075 T651 алюминиевая пластина is a high-strength, heat-treatable aluminum alloy belonging to the Al-Zn-Mg-Cu series. “7075” represents the alloy number, while “T651” refers to the state of the alloy after a specific heat treatment and pre-stretching process (Temper 6, Stretch 1). This process not only improves the strength and toughness of the material, but also enhances its resistance to stress corrosion cracking.
7075 T651 Aircraft Aluminum Plate has the following notable characteristics:
High strength: As one of the strongest commercial alloys, 7075 T651 Aircraft Aluminum Plate is much stronger than mild steel and is one of the best performing aluminum alloys.
Its tensile strength can reach 572MPa and its yield strength can reach 503MPa, making it suitable for high-stress structural parts.
Good mechanical properties: In addition to high strength, the alloy also has good mechanical properties, including wear resistance, fatigue resistance and impact resistance.
Easy to process: Although it has high strength, 7075 T651 Aircraft Aluminum Plate has good processability and is suitable for various complex machining operations such as cutting, drilling, bending, etc.
Good corrosion resistance: Through proper heat treatment and surface treatment, 7075 T651 Aircraft Aluminum Plate can effectively resist general corrosion and extend its service life.
Top Metal provides sheets with a maximum width of up to 3800mm and a maximum thickness of 250mm, as well as sheet up to 2650mm wide and as thin as 0.2mm, meeting various orders’ thickness and width requirements.
Product Introduction of 7075 T651 Aircraft Aluminum Plate
| Hot selling temper | O , T6 , T73 , T76 , T65 , T7351 , T7651 | |
| Equivalent names | UNS A97075 , EN AW-7075 , 3.4365 , 7075 A-Z5GU , AlZn6MgCu , 7075 L95 L96 | |
| UNS A97075 aluminum sheet | Thickness:0.01″-0.24″(0.2mm-8mm) | Width:35.4″-104″(900mm-2650mm) |
| 7075 алюминиевая пластина | Thickness:0.32″-9.84″(8mm-250mm) | Width:39.4″-150″(1000mm-3800mm) |
| 7075 Alclad aluminum sheet | Thickness:0.01″-0.24″(0.2mm-6mm) | Width:35.4″-104″(900mm-2650mm) |
| 7075 Ultra wide aluminum plate | Thickness:0.32″-9.84″(8mm-250mm) | Width:39.4”-150”(1000mm-3800mm) |
| Длина | Max 20m, Fix & Cut Length or Customized | |
| Coating | Black and white film, blue film, transparent film(Thickness: 50 microns, 80 microns) | |
| Обработка поверхности | Bright, polished, hair line, brush, sand blast, checkered, embossed, etching, etc. | |
7075 aerospace aluminum sheet is one of the strongest alloys commercially available, and its strength is much higher than ordinary aluminum alloys and many other metal materials. Its tensile strength σb (MPa) reaches or exceeds 560, and its elongation stress σp0.2 (MPa) reaches or exceeds 495, making it capable of withstanding high stress and high-intensity application environments.
7075 aluminum alloy (AA7075) is an aluminum alloy with zinc as the primary alloying element. It has excellent mechanical properties and exhibits good ductility, high strength, toughness, and good resistance to fatigue.
Chalco 7075 алюминиевая пластина physical properties
| СПЛАВ | ХАРАКТЕР | DIRECTION | ТОЛЩИНА (ММ) | TENSILE STRENGTH RM(MPA) | YIELD STRENGTHRP0.2(MPA) | BREAKING ELONGATIONA50% |
| 7075 Thick Aluminum Plate | Т651 | LT | 6-260 | 570-590 | 495-515 | 10-13.5 |
| Т7651 | LT | 6-102 | 550-560 | 480-490 | 10.5-12.5 | |
| Т7351 | LT | 6-102 | 500-520 | 420-435 | 10-12.5 | |
| 7075 Thin Aluminum Plate | Т6 | – | 0.5-3.5 | 550-570 | 480-500 | 10-15 |
7075-O Alclad aluminum plate
7075-T6 aluminum plate
7075-T6 Alclad aluminum plate
7075-T651 aluminum plate
7075-T7351 aluminum plate
QQ-A-250/12 ASTM.B209 AMS.4044
QQ-A-250/12 ASTM.B209 AMS.4048
QQ-A-250/12 AMS.4045 ASTM.B209
QQ-A-250/13 AMS.4049 ASTM.B209
QQ-A-250/12 AMS.4045 ASTM.B209 BSS 7055 CMMP.025
QQ-A250/12 AMS.4078 ASTM.B209 CMMP.025
Because 7075 T651 aluminum plate has so many excellent properties, it is widely used in the aviation industry. The following are its main application areas:
Aircraft structure: used to make key components such as aircraft skin, fuselage frame, beam, rotor, propeller, fuel tank, etc. Its high strength and good mechanical properties can ensure the safety and stability of the aircraft.
Mechanical equipment: In the manufacture of mechanical equipment, 7075 T651 aluminum plate is often used to manufacture high-precision and high-load parts, such as gears, shafts, molds, etc.
Tooling fixtures: Due to its high strength and wear resistance, this alloy is also often used to manufacture auxiliary tools such as tooling fixtures to improve production efficiency and quality.
Automobile manufacturing: In the automotive industry, 7075 T651 aluminum plate is used to manufacture some parts with high strength and lightweight requirements, such as frames, suspension systems, etc.